采用前驱体粉末发泡法,以3,3′,4,4′-二苯甲酮四甲酸二酐(BTDA)、3,3′,4,4′-联苯四羧酸二酐(BPDA)和4,4′-二氨基二苯甲烷(MDA)为原料,制备了一系列的聚酰亚胺泡沫。通过傅里叶红外光谱仪、扫描电镜、热失重分析仪和导热系数测定仪等手段对酯化后的二酐在不同比例下制备的产物形貌、热稳定性、隔热性能等方面进行了表征。结果表明:生成的聚酰亚胺泡沫已完全亚胺化;热失重10%的分解温度均在500℃以上;泡沫的导热系数表明其隔热性能较好。
The polyimide foams (PIFs) were prepared by the foaming of precursor powders,which were derived from the reaction of esters of 3,3′,4,4′-benzophenone tetracarboxylic acid dianhydride (BTDA) and esters of 3,3′,4,4′-biphenyltetracarboxylic dianhydride (BPDA) with 4,4′-diaminodiphenylmethane (MDA).The products were characterized by fourier transform infrared spectroscopy (FT-IR),scanning electron microscopy (SEM),thermal gravimetric analysis (TGA) and thermal conductivity tester.The results showed that the foams were completely imidized.The decomposition temperature of 10wt% of the product was above 500℃.Thermal conductivity data shown that PIFs were good insulation at ambient conditions.
[1] Weiser E S,Johnson T F,St Clair T L,et al.Polyimide foams for aerospace vehicles[J].High Performance Polymers,2016,12(1):1-12.
[2] Williams M K,Holland D B,Melendez O,et al.Aromatic polyimide foams:factors that lead to high fire performance[J].Polymer Degradation and Stability,2005,88(1):20-27.
[3] Wang Y Y,Zhou Z H,Zhou C G,et al.Lightweight and robust carbon nanotube/polyimide foam for efficient and heat-resistant electromagnetic interference shielding and microwave absorption[J].ACS Applied Materials & Interfaces,2020,12(7):8704-8712.
[4] 许云汉,王磊磊,胡爱军,等.耐高温聚酰亚胺泡沫材料[J].化学进展,2018,30(5):684-691.
[5] 李建伟.共聚型聚酰亚胺泡沫材料的制备及其结构与性能研究[D].西安:西北工业大学,2018.
[6] Li J,Yu N,Jing Z,et al.Fabrication of rigid polyimide foams via thermal foaming of nadimide-end-capped polyester-amine precursor[J].Polymer Bulletin,2019,77:5899-5912.
[7] 张莹.耐高温聚酰亚胺结构泡沫材料制备及力学性能研究[D].哈尔滨:哈尔滨工程大学,2018.
[8] Liaw D J,Wang K L,Huang Y C,et al.Advanced polyimide materials:syntheses,physical properties and applications[J].Progress in Polymer Science,2012,37(7):907-974.
[9] Wang L,Hu A,Fan L,et al.Structures and properties of closed-cell polyimide rigid foams[J].Journal of Applied Polymer Science,2013,130(5):3282-3291.
[10] Zhong A,Li J,Zhang Y,et al.Low temperature microwave fabrication of three-dimensional graphene/polyimide foams with flexibility strain responsivity[J].Composites Part A:Applied Science and Manufacturing,2020,137:105995.
[11] Yao Y,Zhang G,Li J,et al.Effects of 4,4′-diaminodiphenyl ether on the structures and properties of isocyanate-based polyimide foams[J].Journal of Applied Polymer Science,2018,135(12):46029.
[12] Liu X A,Zhan M S,Kai W,et al.Preparation and performance of a novel polyimide foam[J].2012,23(3):677-685.
[13] 邱银,汪树军.聚酰亚胺泡沫材料[J].化工新型材料,2003,31(8):15-17.
[14] 郑逸良,黄志成,阎敬灵.聚酰亚胺泡沫材料研究进展[J].塑料科技,2018,46(8):122-127.
[15] 孙高辉.异氰酸酯基聚酰亚胺泡沫材料制备及阻燃性研究[D].哈尔滨:哈尔滨工程大学,2016.
[16] 马明明.聚酰亚胺泡沫塑料的制备与性能表征[D].青岛:青岛科技大学,2011.
[17] Yu F,Wang K,Liu X Y,et al.Preparation and properties of rigid polyimide foams derived from dianhydride and isocyanate[J].Journal of Applied Polymer Science,2013,127(6):5075-5081.
[18] Kuwabara A,Ozasa M,Shimokawa T,et al.Basic mechanical properties of balloon-type TEEK-L polyimide-foam and TEEK-L filled aramid-honeycomb core materials for sandwich structures[J].Advanced Composite Materials,2005,14(4):343-363.
[19] Li J,Zhang G,Li J,et al.Preparation and properties of polyimide/chopped carbon fiber composite foams[J].Polymers for Advanced Technologies,2017,28(1):28-34.
[20] 酒永斌,翟宇,王方颉,等.前驱体粉末法制备聚酰亚胺泡沫压缩变形研究[J].化工新型材料,2017,45(11):109-111.
[21] 马晶晶,赵一搏,酒永斌,等.硬质芳香族聚酰亚胺泡沫的研究进展[J].宇航材料工艺,2019,49(2):1-6.
基金资助
河北省发改委省级省校合作资助项目(2016049822)
PDF